Tri-colour silk finish in Red, Yellow & Green | Smooth, lustrous surface quality | Wide printing speed range of 50–250 mm/s | Compatible with 0.4 mm nozzles and above | 1 kg spool
The Anycubic PLA Silk Tri-Color Filament in Red, Yellow and Green is designed for makers who want to add visual depth and a premium silk-like lustre to their FDM prints. The tri-colour construction blends three distinct hues across the filament strand, producing layered gradients and rich colour transitions that give finished models a sophisticated, eye-catching texture. It works with any FDM printer fitted with a 0.4 mm or larger nozzle, with a recommended printing temperature of 210–240 °C, a heated bed set to 55–56 °C, and a print speed range of 50–250 mm/s. Luster is also controllable: higher nozzle temperatures and slower print speeds increase filament fluidity, resulting in a smoother, higher-gloss surface. Each spool weighs 1 kg and should be dried at 55–65 °C for 6–8 hours before use for best results — a reliable material for decorative parts, fan art, and display models.
Features
- Tri-colour filament combines Red, Yellow, and Green for rich gradient and layered visual effects
- 1kg spool for extended printing sessions and larger projects
- PLA-based material — easy to print and widely compatible with FDM printers
- Intelligent identification chip compatible with Anycubic ACE Pro for automatic filament recognition
- Resilient and flexible — tested to resist breakage during feeding and multi-colour operation
- Prints at 210–240 °C nozzle temperature; heated bed at 55–56 °C
- Recommended print speed: 50–250 mm/s
- Reusable filament spool with threaded locking system to reduce entanglement
Specifications
- Colour: Red Yellow Green
- Package Weight: 1 kg
- Dry Out Before Use: Recommended
- Drying Condition: 55-65℃, 6-8h
- ACE Compatibility: Compatible
- Nozzle Size: Recommended 0.4 mm or above
- Printing Temperature: 210-240 ℃
- Heated Bed Temperature: 55-56 ℃
- Recommended Printing Speed: 50-250 mm/s
- Maximum Volume Speed (Flow Rate): 8 mm³/s
- Density: 1.22 g/cm³
- Melt Index: 9±1 g/10 min (190℃/2.16kg)
- Melting Point Temperature: 164 ℃
- Vicat Softening Temperature: 54 ℃
- Heat Deflection Temperature (0.45MPa): 53 ℃
- Young’s Modulus: 2000±200 MPa
- Tensile Strength: 37±4 MPa
- Elongation at Break: 28±5%
- Bending Modulus: 2400±160 MPa
- Bending Strength: 66±4 MPa
- lzod lmpact Strength (X-Y): 20±2 kJ/m²
- Tensile Strength (Z): 12±4 MPa
- Filament Type: Aesthetic filaments
- Recommend to Print: Decorative parts, fandom, artworks
- Intelligent Identification: Supported
- Reusable Filament Spool: Supported
What's in the Box
- Anycubic PLA Silk Tri-Color Filament – Red Yellow Green x1