Silk-lustre dual-colour PLA filament | Gradient pink and gold finish | Adjustable gloss via print settings | Compatible with 0.4 mm nozzles and above | Suitable for decorative prints and artistic models
The Anycubic PLA Silk Dual Filament in Pink/Gold is designed for makers who want their prints to stand out with a rich, multi-tonal finish. The dual-colour silk formulation blends pink and gold tones into a gradient effect that shifts as the model is rotated, lending finished pieces a premium, layered appearance suited to decorative parts, fan art, and artistic projects. You can fine-tune the surface gloss by adjusting nozzle temperature and print speed — a higher temperature or slower speed increases filament fluidity, producing a smoother, higher-gloss result. The filament prints at 210–240 °C with a heated bed set to 55–56 °C and accommodates speeds of 50–250 mm/s, giving you the flexibility to balance quality and throughput. Use a 0.4 mm nozzle or larger for best results, and dry the filament at 55–65 °C for 6–8 hours before use to ensure consistent extrusion.
Features
- Dual-colour Pink/Gold silk finish creates a gradient, multi-tonal effect that shifts with viewing angle
- Adjustable luster — increase nozzle temperature or reduce print speed for a higher-gloss, silky surface
- Printing temperature range of 210–240 °C suits a wide variety of FDM printers with a 0.4 mm or larger nozzle
- Recommended print speed of 50–250 mm/s for flexible throughput without sacrificing surface quality
- Heated bed temperature of 55–56 °C for reliable first-layer adhesion
- Dry before use at 55–65 °C for 6–8 hours to maintain filament integrity and consistent flow
- Complies with RoHS, REACH, and SDS certifications
Specifications
- Colour: Pink Gold (#F67599,#F2A900)
- Dry Out Before Use: Recommended
- Drying Condition: 55-65℃, 6-8h
- ACE Compatibility: Compatible
- Nozzle Size: Recommended 0.4 mm or above
- Printing Temperature: 210-240 ℃
- Heated Bed Temperature: 55-56 ℃
- Recommended Printing Speed: 50-250 mm/s
- Maximum Volume Speed (Flow Rate): 8 mm³/s
- Density: 1.22 g/cm³
- Melt Index: 9±1 g/10 min (190℃/2.16kg)
- Melting Point Temperature: 164 ℃
- Vicat Softening Temperature: 54 ℃
- Heat Deflection Temperature (0.45MPa): 53 ℃
- Young's Modulus: 2000±200 MPa
- Tensile Strength: 37±4 MPa
- Elongation at Break: 28±5%
- Bending Modulus: 2400±160 MPa
- Bending Strength: 66±4 MPa
- lzod lmpact Strength (X-Y): 20±2 kJ/m²
- Tensile Strength (Z): 12±4 MPa
- Filament Type: Aesthetic filaments
- Recommend to Print: Decorative parts, fandom, artworks
- Intelligent Identification: Supported
- Reusable Filament Spool: Supported
- Size: 1KG